Two-part; gray; heat cure
Unit of Measure
Specifications
Type |
N/A Thermally Conductive Adhesives |
Product Form |
N/A Two-Part |
Color |
N/A Gray |
Viscosity |
N/A 11000 mPa/s |
Durometer |
N/A 72 A |
Tensile Strength |
N/A 400 psi2.76 MPa28.1 kgf/cm² |
Elongation |
N/A 35 % |
Specific Gravity |
N/A 2.3 |
Compression Modulus at 10 % |
N/A 125 psi |
Linear CTE |
N/A 179 µ/mC |
| Working Time at Room Temperature1 | N/A 2 h |
| Room Temperature Cure Time2 | N/A Material will cure after 24+ hours at room temperature, but requires heat cure for chemical bonding adhesion. |
| Heat Cure Time at 100 ºC (212 ºF)3 | N/A 50 min |
| Heat Cure Time at 125 ºC (257 ºF)4 | N/A 40 min |
| Heat Cure Time at 150 ºC (302 ºF)5 | N/A 10 min |
Unprimed Adhesion Lap Shear |
N/A 540 psi372 N/cm²37.9 kgf/cm² |
| Thermal Conductivity6 | N/A 1.4 W/m·K |
Shelf Life from Date of Manufacture |
N/A 12 months |
Dielectric Strength |
N/A 454 V/mil17.9 kV/mm |
Dielectric Constant at 100 Hz |
N/A 4.7 |
Dielectric Constant at 100 kHz |
N/A 4.7 |
Dissipation Factor at 100 Hz |
N/A 0.0045 |
Dissipation Factor at 100 kHz |
N/A 0.00013 |
Volume Resistivity |
N/A 7.2E+13 O/cm |
Features
|
N/A
|
- 1 Time to double initial mixed viscosity.
- 2 Cure time for 3 mm thickness at 20 °C (68 °F) and 55 % relative humidity.
- 3 Time to 90 percent of final hardness and adhesion or 90 % of curve height for elastic modulus; additional time may be required for the part to warm to near oven temperature.
- 4 Time to 90 percent of final hardness and adhesion or 90 % of curve height for elastic modulus; additional time may be required for the part to warm to near oven temperature.
- 5 Time to 90 percent of final hardness and adhesion or 90 % of curve height for elastic modulus; additional time may be required for the part to warm to near oven temperature.
- 6 Thermal Conductivity at 25 ºC (77 ºF)