One-part; low flow; gray
Unit of Measure
Specifications
Type |
N/A Thermally Conductive Adhesives |
Product Form |
N/A One-Part |
Color |
N/A Gray |
Viscosity |
N/A 58000 mPa/s |
Durometer |
N/A 92 A |
Tensile Strength |
N/A 900 psi6.2 MPa63.3 kgf/cm² |
Elongation |
N/A 20 % |
Specific Gravity |
N/A 2.7 |
Linear CTE |
N/A 126 µ/mC |
| Heat Cure Time at 100 ºC (212 ºF)1 | N/A 90 min |
| Heat Cure Time at 125 ºC (257 ºF)2 | N/A 30 min |
| Heat Cure Time at 150 ºC (302 ºF)3 | N/A 20 min |
Unprimed Adhesion Lap Shear |
N/A 640 psi440 N/cm²45 kgf/cm² |
| Thermal Conductivity4 | N/A 1.9 W/m·K |
Shelf Life from Date of Manufacture |
N/A 6 months at 5 ºC |
Dielectric Strength |
N/A 425 V/mil16.7 kV/mm |
Dielectric Constant at 100 Hz |
N/A 4.98 |
Dielectric Constant at 100 kHz |
N/A 4.86 |
Dissipation Factor at 100 Hz |
N/A 0.008 |
Dissipation Factor at 100 kHz |
N/A < 0.003 |
Volume Resistivity |
N/A 2.20E+14 O/cm |
- 1 Time to 90 percent of final hardness and adhesion or 90 % of curve height for elastic modulus; additional time may be required for the part to warm to near oven temperature.
- 2 Time to 90 percent of final hardness and adhesion or 90 % of curve height for elastic modulus; additional time may be required for the part to warm to near oven temperature.
- 3 Time to 90 percent of final hardness and adhesion or 90 % of curve height for elastic modulus; additional time may be required for the part to warm to near oven temperature.
- 4 Thermal Conductivity at 25 ºC (77 ºF)