| Items |
 /Asset/a1123.jpg HCS10 THERM-A-GAP™ - Thermally Conductive Gap Filler Pads |
/Asset/a1123.jpg 569 THERM-A-GAP™ - Thermally Conductive Gap Filler Pads |
/Asset/a1123.jpg 570 THERM-A-GAP™ - Thermally Conductive Gap Filler Pads |
/Asset/a1123.jpg 579-Gap Filler THERM-A-GAP™ - Thermally Conductive Gap Filler Pads |
/Asset/a1123.jpg 580 THERM-A-GAP™ - Thermally Conductive Gap Filler Pads |
|||||
| Test Method Color | Visual | |||||||||
| Color | Orange | Gray | Blue | Pink | Yellow | |||||
| Carrier | Aluminum foil - with PSA Woven glass - no PSA | |||||||||
| Test Method Thicknesses | ASTM D374 | |||||||||
| Standard Thickness1 | 0.25–5.0 mm0.010–0.200 in | 0.25–5.0 mm0.010–0.200 in | 0.5–5.0 mm0.020–0.200 in | 0.25–5.0 mm0.010–0.200 in | 0.5–5.0 mm0.020–0.200 in | |||||
| Test Method Specific Gravity | ASTM D792 | |||||||||
| Specific Gravity | 2.0 | 2.2 | 2.2 | 2.9 | 2.9 | |||||
| Test Method Hardness | ASTM D2240 | |||||||||
| Hardness, Shore 00 | 4 | 10 | 25 | 30 | 45 | |||||
| Test Method Extractable Silicone | Chomerics | |||||||||
| Extractable Silicone | 10 % | 10 % | 6 % | 6 % | ||||||
| Test Method Percent Deflection at Various Pressures | ASTM C165 MOD (0.125 in “G” Type, 0.50 in dia. probe, 0.025 in/min rate) | |||||||||
| Percent Deflection at Various Pressures (0.125 in) at 34 kPa (5 psi) Deflected | 26 % | 20 % | 10 % | 22 % | 7 % | |||||
| Percent Deflection at Various Pressures (0.125 in) at 69 kPa (10 psi) Deflected | 36 % | 30 % | 15 % | 33 % | 10 % | |||||
| Percent Deflection at Various Pressures (0.125 in) at 172 kPa (25 psi) Deflected | 59 % | 50 % | 25 % | 55 % | 20 % | |||||
| Percent Deflection at Various Pressures (0.125 in) at 345 kPa (50 psi) Deflected | 73 % | 35 % | 35 % | 68 % | 30 % | |||||
| Operating Temperature Range | –55 to 200 ºC–67 to 392 ºF | |||||||||
| Test Method Thermal Impedance | ASTM D5470 | |||||||||
| Thermal Impedance at 10 psi, at 1mm Thickness, G Version | 9.7 ºC-cm²/W1.5 ºC-in²/W | 9.1 ºC-cm²/W1.4 ºC-in²/W | 9.1 ºC-cm²/W1.4 ºC-in²/W | 4.5 ºC-cm²/W0.7 ºC-in²/W | 4.5 ºC-cm²/W0.7 ºC-in²/W | |||||
| Test Method Thermal Conductivity | ASTM D5470 | |||||||||
| Thermal Conductivity | 1 W/m·K | 1.5 W/m·K | 1.5 W/m·K | 3 W/m·K | 3 W/m·K | |||||
| Test Method Heat Capacity | ASTM E1269 | |||||||||
| Heat Capacity | 1 J/g-K | |||||||||
| Test Method Coefficient of Thermal Expansion | ASTM E831 | |||||||||
| Coefficient of Thermal Expansion | 250 ppm/K | 250 ppm/K | 150 ppm/K | 150 ppm/K | ||||||
| Test Method Dielectric Strength | ASTM D149 | |||||||||
| Dielectric Strength | 8 KVac/mm200 Vac/mil | |||||||||
| Test Method Volume Resistivity | ASTM D257 | |||||||||
| Volume Resistivity | 1014 O/cm | |||||||||
| Test Method Dielectric Constant | ASTM D150 | |||||||||
| Dielectric Constant at 1000 kHz | 5.3 | 6.5 | 6.5 | 8.0 | 8.0 | |||||
| Test Method Dissipation Factor | Chomerics Test | |||||||||
| Dissipation Factor at 1000 kHz | 0.013 | 0.013 | 0.013 | 0.010 | 0.010 | |||||
| Conformability Rating | 1 | 1 | ||||||||
| Test Method Flammability Rating | UL 94 | |||||||||
| Flammability Rating | Not tested | V-0 | V-0 | V-0 | V-0 | |||||
| Test Method RoHS Compliant | Chomeric Certification | |||||||||
| RoHS Compliant | Yes | |||||||||
| Test Method Outgassing | ASTM E595 | |||||||||
| Outgassing TML | 0.44 % | 0.42 % | 0.35 % | 0.19 % | 0.18 % | |||||
| Outgassing CVCM | 0.13 % | 0.08 % | 0.09 % | 0.06 % | 0.05 % | |||||
| Test Method Shelf Life | Chomerics | |||||||||
| Shelf Life, Months from Date of Shipment G | 24 | |||||||||
| Shelf Life, Months from Date of Shipment A | 18 | |||||||||
|
||||||||||