Type
|
|
Thermally Conductive Materials for Pad Manufacturing
|
|
|
|
Product Form
|
|
Two-Part
|
|
|
|
Color
|
|
Gray
|
|
|
|
Viscosity
|
|
5600 mPa/s
|
|
|
|
Durometer
|
|
70 OO
|
|
|
|
Penetration (1/10 of mm)
|
|
35
|
|
|
|
Tensile Strength
|
|
60 psi
0.4 MPa
4.2 kgf/cm²
|
|
|
|
Elongation
|
|
400 %
|
|
|
|
Specific Gravity
|
|
2.2
|
|
|
|
Linear CTE
|
|
174 µ/mC
|
|
|
|
Working Time at Room Temperature1
|
|
4 h
|
|
|
|
Room Temperature Cure Time2
|
|
7 h
|
|
|
|
Heat Cure Time at 100 ºC (212 ºF)3
|
|
3.5 min
|
|
|
|
Heat Cure Time at 125 ºC (257 ºF)4
|
|
2.5 min
|
|
|
|
Heat Cure Time at 150 ºC (302 ºF)5
|
|
1.9 min
|
|
|
|
Thermal Conductivity6
|
|
0.95 W/m·K
|
|
|
|
Shelf Life from Date of Manufacture
|
|
8 months
|
|
|
|
Dielectric Strength
|
|
455 V/mil
17.9 kV/mm
|
|
|
|
Dielectric Constant at 100 Hz
|
|
4.6
|
|
|
|
Dielectric Constant at 100 kHz
|
|
4.6
|
|
|
|
Dissipation Factor at 100 Hz
|
|
0.002
|
|
|
|
Dissipation Factor at 100 kHz
|
|
0.00015
|
|
|
|
Volume Resistivity
|
|
1.90E+14 O/cm
|
|
|
1 Time to double initial mixed viscosity.
2 Cure time for 3 mm thickness at 20 °C (68 °F) and 55 % relative humidity.
3 Time to 90 percent of final hardness and adhesion or 90 % of curve height for elastic modulus; additional time may be required for the part to warm to near oven temperature.
4 Time to 90 percent of final hardness and adhesion or 90 % of curve height for elastic modulus; additional time may be required for the part to warm to near oven temperature.
5 Time to 90 percent of final hardness and adhesion or 90 % of curve height for elastic modulus; additional time may be required for the part to warm to near oven temperature.
6 Thermal Conductivity at 25 ºC (77 ºF)
|
|