Type
|
|
Thermally Conductive Adhesives
|
|
|
|
Product Form
|
|
Two-Part
|
|
|
|
Color
|
|
Gray
|
|
|
|
Viscosity
|
|
50000 mPa/s
|
|
|
|
Durometer
|
|
66 A
|
|
|
|
Tensile Strength
|
|
508 psi
3.5 MPa
35.7 kgf/cm²
|
|
|
|
Elongation
|
|
110 %
|
|
|
|
Specific Gravity
|
|
2.13
|
|
|
|
Working Time at Room Temperature1
|
|
16 h
|
|
|
|
Heat Cure Time at 100 ºC (212 ºF)2
|
|
60 min
|
|
|
|
Heat Cure Time at 150 ºC (302 ºF)3
|
|
30 min
|
|
|
|
Thermal Conductivity4
|
|
0.74 W/m·K
|
|
|
|
Shelf Life from Date of Manufacture
|
|
12 months
|
|
|
|
Dielectric Strength
|
|
635 V/mil
25 kV/mm
|
|
|
|
Dielectric Constant at 100 kHz
|
|
4.5
|
|
|
|
Dissipation Factor at 100 kHz
|
|
0.0013
|
|
|
|
Volume Resistivity
|
|
1.90E+14 O/cm
|
|
|
1 Time to double initial mixed viscosity.
2 Time to 90 percent of final hardness and adhesion or 90 % of curve height for elastic modulus; additional time may be required for the part to warm to near oven temperature.
3 Time to 90 percent of final hardness and adhesion or 90 % of curve height for elastic modulus; additional time may be required for the part to warm to near oven temperature.
4 Thermal Conductivity at 25 ºC (77 ºF)
|
|