Type
|
|
Thermally Conductive Adhesives
|
|
|
|
Product Form
|
|
One-Part
|
|
|
|
Color
|
|
Gray
|
|
|
|
Viscosity
|
|
68700 mPa/s
|
|
|
|
Durometer
|
|
88 A
|
|
|
|
Tensile Strength
|
|
625 psi
4.3 MPa
43.9 kgf/cm²
|
|
|
|
Elongation
|
|
20 %
|
|
|
|
Specific Gravity
|
|
2.6
|
|
|
|
Linear CTE
|
|
137 µ/mC
|
|
|
|
Heat Cure Time at 100 ºC (212 ºF)1
|
|
60 min
|
|
|
|
Heat Cure Time at 125 ºC (257 ºF)2
|
|
45 min
|
|
|
|
Heat Cure Time at 150 ºC (302 ºF)3
|
|
10 min
|
|
|
|
Unprimed Adhesion Lap Shear
|
|
510 psi
352 N/cm²
35.9 kgf/cm²
|
|
|
|
Thermal Conductivity4
|
|
1.8 W/m·K
|
|
|
|
Shelf Life from Date of Manufacture
|
|
6 months
|
|
|
|
Dielectric Strength
|
|
395 V/mil
15.6 kV/mm
|
|
|
|
Dielectric Constant at 100 Hz
|
|
5.6
|
|
|
|
Dielectric Constant at 100 kHz
|
|
5.5
|
|
|
|
Dissipation Factor at 100 Hz
|
|
0.0059
|
|
|
|
Dissipation Factor at 100 kHz
|
|
< 0.0002
|
|
|
|
Volume Resistivity
|
|
6.85E+13 O/cm
|
|
|
1 Time to 90 percent of final hardness and adhesion or 90 % of curve height for elastic modulus; additional time may be required for the part to warm to near oven temperature.
2 Time to 90 percent of final hardness and adhesion or 90 % of curve height for elastic modulus; additional time may be required for the part to warm to near oven temperature.
3 Time to 90 percent of final hardness and adhesion or 90 % of curve height for elastic modulus; additional time may be required for the part to warm to near oven temperature.
4 Thermal Conductivity at 25 ºC (77 ºF)
|
|