Type
|
|
Thermally Conductive Adhesives
|
|
|
|
Product Form
|
|
One-Part
|
|
|
|
Color
|
|
Gray
|
|
|
|
Viscosity
|
|
58000 mPa/s
|
|
|
|
Durometer
|
|
92 A
|
|
|
|
Tensile Strength
|
|
900 psi
6.2 MPa
63.3 kgf/cm²
|
|
|
|
Elongation
|
|
20 %
|
|
|
|
Specific Gravity
|
|
2.7
|
|
|
|
Linear CTE
|
|
126 µ/mC
|
|
|
|
Heat Cure Time at 100 ºC (212 ºF)1
|
|
90 min
|
|
|
|
Heat Cure Time at 125 ºC (257 ºF)2
|
|
30 min
|
|
|
|
Heat Cure Time at 150 ºC (302 ºF)3
|
|
20 min
|
|
|
|
Unprimed Adhesion Lap Shear
|
|
640 psi
440 N/cm²
45 kgf/cm²
|
|
|
|
Thermal Conductivity4
|
|
1.9 W/m·K
|
|
|
|
Shelf Life from Date of Manufacture
|
|
6 months at 5 ºC
|
|
|
|
Dielectric Strength
|
|
425 V/mil
16.7 kV/mm
|
|
|
|
Dielectric Constant at 100 Hz
|
|
4.98
|
|
|
|
Dielectric Constant at 100 kHz
|
|
4.86
|
|
|
|
Dissipation Factor at 100 Hz
|
|
0.008
|
|
|
|
Dissipation Factor at 100 kHz
|
|
< 0.003
|
|
|
|
Volume Resistivity
|
|
2.20E+14 O/cm
|
|
|
1 Time to 90 percent of final hardness and adhesion or 90 % of curve height for elastic modulus; additional time may be required for the part to warm to near oven temperature.
2 Time to 90 percent of final hardness and adhesion or 90 % of curve height for elastic modulus; additional time may be required for the part to warm to near oven temperature.
3 Time to 90 percent of final hardness and adhesion or 90 % of curve height for elastic modulus; additional time may be required for the part to warm to near oven temperature.
4 Thermal Conductivity at 25 ºC (77 ºF)
|
|