Translucent; 2-part (10:1 mix ratio); heat cure; non-flow after dispensing process; long working time after 2-part mix – reducing need for equipment purge/clean-up; high tensile strength; cure can be accelerated with elevated temperatures for faster processing; room temperature storage
Unit of Measure

Specifications

Type

N/A Two-Part Heat Cure

One or Two Part

N/A 2

Color

N/A Translucent

Viscosity/Flowability

N/A 610000

Durometer

N/A 46 JIS A

Tensile Strength

N/A 1000 psi6.9 MPa70 kgf/cm²

Elongation

N/A 420 %

Working Time at Room Temperature

N/A 8 h

Heat Cure Time

N/A 30 min at 150 ºC

Unprimed Adhesion Lap Shear

N/A 420 psi290 (AL) N/cm²29.5 kgf/cm²

Shelf Life from Date of Manufacture

N/A 18 months at < 30 ºC

Dielectric Strength

N/A 550 V/mil22 kV/mm

Dielectric Constant at 1 MHz

N/A 3

Dissipation Factor at 1 MHz

N/A 1.00E-03

Volume Resistivity

N/A 5.0E+14 O/cm

Agency Listing

N/A NA

Features

N/A
Non-flowing; 10:1 mix ratio; heat cure; high tensile strength; good working time after mixing

Potential or Typical Uses

N/A
Sealing ceramic condensers; sealing electronic components; bonding agent for key pad of PCs