Item # 700, Silicone Solid Rubber Tape On Robert McKeown Co., Inc.

COHRlastic solid silicone rubber in square sheet and continuous length form has a smooth, blemish-free surface. It is available in degrees of hardness from relatively soft 30 durometer to the relatively hard 70 durometer on the Shore A scale. It is manufactured in different formulations to provide a choice of physical properties and cost considerations.

Series 300-700 COHRlastic generalpurpose molded sheet is available in thicknesses up to 1/2" and it withstands temperatures from –100 °F to +500more

Unit of Measure

Specifications

Dielectric Strength Approx.	N/A 500 V/mil
Thermal Conductivity (Average)	N/A 4.4 x 10^-4 x (cal·cm/ºC·cm·s) 1.3 BTU i./h·ft² ºF
Specific Heat	N/A 0.3 BTU/lb/ºF
Linear Thermal Expansion¹	N/A 1.5 x 10^-4
Width/Sheet Size	N/A 36 x 36 in
Color	N/A Red
Thickness²	N/A 1/16 ±.016 in1/2 ±.016 in1/4 ±.016 in1/8 ±.016 in3/16 ±.016 in3/32 ±.016 in3/8 ±.016 in5/16 ±.016 in
ZZ-R-765, Class 2a & 2b (Grade)	N/A 70
AMS	N/A 3304
Test Method Durometer	N/A D2240
Durometer (Shore A ±5)³	N/A 70
Test Method Tensile Strength	N/A D412
Tensile Strength⁴	N/A 700 psi
Test Method Elongation	N/A D412
Elongation⁵	N/A 160 %
Test Method Tear Strength	N/A D624
Tear Strength⁶	N/A 60 ppi
Test Method Compression Set	N/A D395
Compression Set after 70 h at 320 ºF⁷	N/A 15 %
Durometer Change (Points, Shore A) after Dry Heat Aging for 70 h at 437 ºF	N/A +5
Tensile Strength Change after Dry Heat Aging for 70 h at 437 ºF	N/A –15 %
Elongation Change after Dry Heat Aging for 70 h at 437 ºF	N/A –15 %
Durometer Change (Points, Shore A) after Immersion in ASTM Oil #1 (High Aniline Point) for 70 H at 302 ºF	N/A –10
Tensile Strength Change after Immersion in ASTM Oil #1 (High Aniline Point) for 70 H at 302 ºF	N/A –10 %
Elongation Change after Immersion in ASTM Oil #1 (High Aniline Point) for 70 H at 302 ºF	N/A –10 %
Volume Change after Immersion in ASTM Oil #1 (High Aniline Point) for 70 H at 302 ºF	N/A +5 %

¹ Room temperature to +350 ºF
² Thickness 3/32 in - special order. Minimum quantities apply.
³ Die B Method B, ASTM D2000 + Fed. Spec. ZZ-R-765.
⁴ Die B Method B, ASTM D2000 + Fed. Spec. ZZ-R-765.
⁵ Die B Method B, ASTM D2000 + Fed. Spec. ZZ-R-765.
⁶ Die B Method B, ASTM D2000 + Fed. Spec. ZZ-R-765.
⁷ Die B Method B, ASTM D2000 + Fed. Spec. ZZ-R-765.

Specifications

Dielectric Strength Approx.

Thermal Conductivity (Average)

Specific Heat

Width/Sheet Size

Color

ZZ-R-765, Class 2a & 2b (Grade)

AMS

Test Method Durometer

Test Method Tensile Strength

Test Method Elongation

Test Method Tear Strength

Test Method Compression Set

Durometer Change (Points, Shore A) after Dry Heat Aging for 70 h at 437 ºF

Tensile Strength Change after Dry Heat Aging for 70 h at 437 ºF

Elongation Change after Dry Heat Aging for 70 h at 437 ºF

Durometer Change (Points, Shore A) after Immersion in ASTM Oil #1 (High Aniline Point) for 70 H at 302 ºF

Tensile Strength Change after Immersion in ASTM Oil #1 (High Aniline Point) for 70 H at 302 ºF

Elongation Change after Immersion in ASTM Oil #1 (High Aniline Point) for 70 H at 302 ºF

Volume Change after Immersion in ASTM Oil #1 (High Aniline Point) for 70 H at 302 ºF